. Embrittlement of duplex stainless steels SAF 2205 y SAF 2507 subjected to artificial aging heat treatments
DOI:
https://doi.org/10.54139/revinguc.v28i1.7Keywords:
microstructure, annealing, ultimate tensile stress, elongation, toughness.Abstract
The research studies the embrittlement of SAF 2205 and SAF 2507 duplex stainless steels subjected to artificial aging treatments. Artificial aging treatments were performed Charpy V-shaped tensile and impact specimens, the treatment consisted of two phases, first the solubilization of the steels was carried at temperatures between 1100 °C and 1200 °C with times between 1 h and 2 h, and second, the artificial aging was carried out at temperatures of 475 °C, 700 °C, 850 °C, 870 °C, and 900 °C. There are several factors that affect the mechanical characteristics of stainless steels, for example, the existence of micro-segregations and the precipitation of secondary phases, which can take place during solidification, shaping, heat treatment, welding operations, etc. The study carried out allowed the construction of curves that show the changed in the mechanical behavior obtained from the SAF 2205 and SAF 2507 duplex steels, where it is observed that as aging time increases, ductility, mechanical strength, and impact toughness are reduced. In the microstructure was observed the precipitation of sigma and Chi secondary phases.
Downloads
References
Asociación Internacional de Molibdeno , Directrices prácticas para la fabricación de los aceros inoxidables dúplex. Londres, Reino Unido: International Molybdenum Association(IMOA), 2012.
J. Nilsson, "Super Duplex Stainless Steels," Materials Science and Technology, vol. 8, no. 8, pp. 685-700, 1992. https://doi.org/10.1179/mst.1992.8.8.685
J. Charles, "Superduplex, stainless steels: structure and properties," in Duplex stainless steels'91, vol. 1. Les Ulis, France: Les Editions de Physique, 1991.
M. Pohl, O. Storz, and T. Glogowski, "Effect of intermetallic precipitations on the properties of duplex stainless steel," Materials Characterization, vol. 58, no. 1, pp. 65-71, 2007. https://doi.org/10.1016/j.matchar.2006.03.015
F. M. Elsabbagh, R. M. Hamouda, and M. A. Taha, "On microstructure and microhardness of isothermally aged UNS S32760 and the effect on toughness and corrosion behavior," Journal of Materials Engineering and Performance, vol. 25, pp. 275-284, 2014. https://doi.org/10.1007/s11665-013-0619-7
N. Llorca-Isern, I. López-Jiménez, H. López-Luque, M. V. Biezma, and A. Roca, "Study of the precipitation of secondary phases in duplex and superduplex stainless steel," in Materials Science Forum, vol. 879. Trans Tech Publications, 2017. https://doi.org/10.4028/www.scientific.net/MSF.879.2537
S.-K. Kim, K.-Y. Kang, M.-S. Kim, and J.-M. Lee, "Low-Temperature Mechanical Behavior of Super Duplex Stainless Steel with Sigma Precipitation," Metals, vol. 5, no. 3, pp. 1732-1745, 2015. https://doi.org/10.3390/met5031732
P. Ferro, F. Bonollo, and G. Timelli, "Sigma phase precipitation modelling in a UNS S32760 superduplex stainless steel," La Metallurgia Italiana, vol. 104, no. 5, pp. 7-12, 2012.
S. K. Ghosh and S. Mondal, "High temperature ageing behavior of a duplex stainless-steel material," Materials Characterization, vol. 59, no. 12, pp. 1776-1783, 2008. https://doi.org/10.1016/j.matchar.2008.04.008
S. Topolska and J. Lawanoski, "Effect of microstructure on impact toughness of duplex and super duplex stainless steel," Journal of Achievements in Materials and Manufacturing Engineering, vol. 36, no. 2, 2009.
ASTM A 370, Standard Test Methods and Definitions for Mechanical Testing of Steel Products, American Society for Testing and Materials, USA, 2018.
ASTM E 23, Test Methods for Notched Bar Impact Testing of Metallic Materials, American Society for Testing and Materials, USA, 2014.
L. Sáenz, "Naturaleza fractal de la deformación plástica de un acero inoxidable dúplex envejecido," Revista Ingeniería y Sociedad, 2011.
J. Griman and J. Marcano, "Evaluación de la tenacidad de impacto del acero inoxidable dúplex SAF 2205 sometido a un tratamiento térmico de envejecimiento 475 °C," Trabajo de Grado de Ingeniería Mecánica, Facultad de Ingeniería, Universidad de Carabobo, Venezuela, 2005.
L. Grippi and A. Ocando, "Evaluación de la tenacidad de impacto del acero inoxidable dúplex SAF 2205 sometido a un tratamiento térmico de envejecimiento 850 °C con unos tiempos de 48, 54 y 60 minutos," Trabajo de Grado de Ingeniería Mecánica, Facultad de Ingeniería, Universidad de Carabobo, Venezuela, 2006.
L. Plaza, "Evaluación de la tenacidad de impacto de un acero inoxidable dúplex SAF 2205 sometido a un tratamiento térmico de envejecimiento a una temperatura de 850 °C, con unos tiempos de 6,12 y 24 horas," Trabajo de Grado de Ingeniería Mecánica, Facultad de Ingeniería, Universidad de Carabobo, Venezuela, 2007.
M. Mosquera and R. Tiamo, "Evaluación de la tenacidad de impacto de un acero inoxidable duplex SAF 2507 sometido a un tratamiento térmico de envejecimiento a una temperatura de 700 °C," Trabajo de Grado de Ingeniería Mecánica, Facultad de Ingeniería, Universidad de Carabobo, Venezuela, 2008.
L. Sáenz, O. Hilders, and H. R., "Estudio del acero inoxidable dúplex SAF 2507 sometido a un tratamiento térmico de envejecimiento a una temperatura de 850 °C por tiempos entre 1 hora y 48 horas," Revista Facultad de Ingeniería UCV, vol. 22, no. 3, pp. 21-30, 2007.
A. Mejías, J. Arruti, J. Cepeda, and L. Sáenz, "Influencia del tratamiento térmico de envejecimiento sobre las propiedades mecánicas y la microestructura de un acero inoxidable dúplex 2507," Revista Ingeniería UC, vol. 17, no. 3, pp. 28-39, 2010.
J. Arruti, "Determinación de la influencia del tratamiento térmico realizado a una temperatura de 870 °C durante tiempos comprendidos entre 2 y 10 minutos sobre las propiedades mecánicas y la microestructura de un acero inoxidable dúplex," Trabajo de Grado de Maestría, Universidad de Carabobo, Venezuela, 2009.
A. Mejías, "Evaluación de la tenacidad de impacto de un acero inoxidable dúplex SAF 2507 sometido a un tratamiento térmico de envejecimiento a una temperatura de 900 °C," Trabajo de Grado de Maestría, Universidad de Carabobo, Venezuela, 2009.
J. Cepeda, "Determinación de la influencia del tratamiento térmico realizado a una temperatura de 685 °C sobre las propiedades mecánicas y la microestructura de un acero inoxidable dúplex SAF 2507," Trabajo de Grado de Maestría, Universidad de Carabobo, Venezuela, 2009.
J. Hau and A. Seijas, Eds., Sigma Phase Embrittlement of stainless steel in FCC Service. NACE 61st Annual Conference & Exposition, no. 6578. NACE, 2006.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Revista Ingeniería UC
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.